<p>環(huán)氧樹脂具有粘結性好、強度高、無毒、常溫固化、可發(fā)泡以及穩(wěn)定性好等特點。以其為基料，添加空心微珠，并用鋁粉發(fā)泡，可制成環(huán)氯泡沫保溫材料。這種保溫材料具有保溫性好、吸水性小、無毒、耐熱性及防火性好等優(yōu)點，并兼有吸聲及阻尼效果。該材料的研究和應用，彌補了我國有機保溫材料防火性差、有毒性以及適用范圍窄等不足。它在建筑、交通、工業(yè)及國防等領域具有廣闊的應用.</p> <p><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: small;">　（1)</span></span><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: small;">雙酚<span>A</span>環(huán)氧樹脂</span><span><br /></span><span style="font-size: small;">   (2)固化劑。采用<span>2</span>種固化劑：聚酰胺固化劑<span>(</span>固化劑<span>-1)</span>及脂肪酸改性多元胺固化劑<span>(</span>固化劑<span>-2)</span>進行實驗。</span><span><br /><span style="font-size: small;">　 (3)</span></span><span style="font-size: small;">發(fā)泡材料。一般國產(chǎn)有機發(fā)泡劑的毒性較大，不能采用；而鋁粉在堿性條件下反應，生成的氫氣及<span>A1(OH)3</span>膠體，均無毒，<span>A1(OH)3</span>還有很好的阻燃性，對提高保溫材料的阻燃性有益。故采用鋁粉和<span>NaOH</span>溶液為發(fā)泡材料。</span><span><br /><span style="font-size: small;">   (4)</span></span><span style="font-size: small;">空心微珠。提高保溫材料孔隙率是改善保溫材料性能的有效措施之一。提高孔隙率可以采用以下<span>2</span>種方法：一是發(fā)泡，二是選用空心填料。單純依靠發(fā)泡來提高孔隙率會造成材料的強度及硬度降低，力學性能下降。因此，在發(fā)泡的同時，有必要引入合適的空心微珠作填料，在不影響力學性能的基礎上，改善保溫性能。常用的空心微珠有：空心玻璃微珠、活性碳、漂珠和酚醛微珠等。實驗時我們對前<span>3</span>種空心微珠進行了研究。空心微珠指標：①空心玻璃微珠：粒徑<span>10~180&micro;m</span>，堆積密度<span>120kg</span>／<span>m3</span>；②活性炭：粒徑<span>1.0~2.5mm</span>，堆積密度<span>250   kg</span>／<span>m3</span>；③漂珠：<span>0</span>．<span>1~1mm</span>，堆積密度<span>260   Kg</span>／<span>m3</span>。</span><span><br /><span style="font-size: small;">   (5)</span></span><span style="font-size: small;">其它材料。采用<span>95</span>％乙醇<span>(</span>工業(yè)純<span>)</span>為稀釋劑.</span><span><br /></span><span style="font-size: small;"><span>  </span></span></span></span></p> <p><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: small;"><span> </span>工藝及成型</span><span><br /></span><span style="font-size: small;">   將環(huán)氧樹脂用乙醇稀釋，加入鋁粉、空心微珠及固化劑，攪拌均勻；然后滴人適量<span>NaOH</span>溶液，迅速攪拌均勻，將形成的混合料注入模具中；混合料在<span>60~110min</span>以內逐漸發(fā)泡、膨脹并硬化成型，脫模后即為所需保溫材料。</span><span><br /></span><span style="font-size: small;">工藝參數(shù)：成型溫度和濕度：<span>10~30<span><span>℃</span></span><span>，相對濕度70</span></span>％<span>~95</span>％；攪拌：轉速<span>300</span>次／<span>min</span>，時間<span>10min</span>；澆注成型，固化時間<span>60~110</span></span></span></span></p> <p><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: small;"></span></span></span> </p> <p><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: 9pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;"><span style="font-size: small;"><span><span style="font-size: 12pt; font-family: 宋體; mso-bidi-font-family: 宋體; mso-ansi-language: EN-US; mso-fareast-language: ZH-CN; mso-bidi-language: AR-SA;">  空心微珠的影響<span><br /></span>解決保溫性能與其它性能矛盾的有效措施是引入空心微珠。空心微珠本身是多子孔的<span>(</span>且孔隙封閉<span>)</span>，堆積密度小，可明顯提高材料的孔隙率，并且填充粗大孔隙，使材料的孔隙構造發(fā)生變化，在改善保溫性能的同時，不會造成吸水率增大或強度降低</span></span></span></span></span></p>